Abstract FR:

DES CERAMIQUES DE Pb₂KNb₅O₁₅ DE STRUCTURE BRONZE QUADRATIQUE DE TUNGSTENE DEFORMEE, ET DES PHASES DERIVEES PB#2(K#1##XLA#X#/#3)NB#5O#1#5 (0<X0,3) ET PB#2K(NB#1##XTA#X)O#1#5 (0<X1) ONT ETE ELABOREES. EN UTILISANT UN FRITTAGE EN ENCEINTE FERMEE, LES PERTES DE MASSE SONT REDUITES ET LA STCHIOMETRIE EST MAINTENUE. LES CERAMIQUES SONT HOMOGENES ET PRESENTENT UNE COMPACITE COMPRISE ENTRE 0,90 ET 0,96 SELON LA COMPOSITION. L'APPLICATION DE LA SPECTROSCOPIE D'IMPEDANCE COMPLEXE A CES MATERIAUX FERROELECTRIQUES PRESENTANT UNE CONDUCTIVITE NOTABLE A CONDUIT A L'OBTENTION D'UNE EXPRESSION RELIANT L'IMPEDANCE ET LA FREQUENCE, QUI PARAIT PLUS GENERALE QUE LES EXPRESSIONS IDEALE DE DEBYE, TRADITIONNELLE DE COLE-COLE ET EMPIRIQUE DE JONSCHER. UNE EXCELLENTE CONCORDANCE ENTRE L'EXPERIENCE ET LA THEORIE EST OBTENUE. DE PLUS, L'ORIGINE DE LA DISPERSION DIELECTRIQUE A BASSE FREQUENCE EST CLAIREMENT ETABLIE A PARTIR DE CE MODELE. L'ETUDE PAR SPECTROSCOPIE DIELECTRIQUE DANS LA GAMME DE FREQUENCE 20-10#9 HZ A REVELE QUE TROIS MECANISMES DE DISPERSION SONT SUSCEPTIBLES DE COEXISTER DANS CES MATERIAUX. LE PREMIER A HAUTE TEMPERATURE ET A BASSE FREQUENCE EST LIE AU DEPLACEMENT DES CHARGES MOBILES. LE SECOND MECANISME N'INTERVIENT QUE DANS L'ETAT FERROELECTRIQUE POUR DES COMPOSES PRESENTANT UNE TRANSITION DE PHASE DIFFUSE. IL AFFECTE UNE GAMME DE FREQUENCE D'AUTANT PLUS LARGE QUE LE MATERIAU EST PLUS DESORDONNE. ENFIN LA RELAXATION OBSERVEE A F<10#8 HZ EST CARACTERISTIQUE DE LA STRUCTURE BRONZE QUADRATIQUE DE TUNGSTENE